fa کلیدزنی Q غیرفعال یک لیزر دمش از پهلوی دیودی Er-Yb:Glass با یک بلور Co2+:MgAl2O4 به‌عنوان جاذب اشباع‌پذیر تخصصی Special پژوهشي Research <table align="center" cellpadding="0" cellspacing="0" hspace="0" vspace="0"> <tbody> <tr> <td style="padding: 0cm; vertical-align: top; text-align: justify;"><span style="font-family:b nazanin;"><span style="font-size:10.0pt;">در این مقاله، طراحی و ساخت یک لیزر دمش دیودی </span></span><span dir="LTR" style="font-weight:normal;"><span style="font-size:9.0pt;">Er-Yb:Glass</span></span> <span style="font-family:b nazanin;"><span style="font-size:10.0pt;">کلیدزنی</span></span><span dir="LTR" style="font-weight:normal;"><span style="font-size:9.0pt;">Q</span></span><span style="font-family:b nazanin;"><span style="font-size:10.0pt;"> شده با بلور</span></span><span dir="LTR" style="font-weight:normal;"><span style="font-size:9.0pt;">Co²⁺:MgAl₂O₄</span></span> &nbsp;<span style="font-family:b nazanin;"><span style="font-size:10.0pt;">گزارش شده است. برای طراحی این لیزر از نرم‌افزار </span></span><span dir="LTR" style="font-weight:normal;"><span style="font-size:10.0pt;">LASCAD</span></span><span style="font-family:b nazanin;"><span style="font-size:10.0pt;"> استفاده شده است و براساس طراحی صورت گرفته یک چیدمان آزمایشگاهی برپاشده است. در نهایت، پالس‌های لیزر با پهنای پالس ۳۰ نانوثانیه و انرژی 15 میلی ژول در توان پمپ ورودی حدود ۲وات به صورت تجربی به‌دست آمده است.</span></span><span dir="LTR" style="font-weight:normal;"><span style="font-size:10.0pt;"></span></span></td> </tr> </tbody> </table> <div style="clear:both;"></div> <table align="center" cellpadding="0" cellspacing="0" hspace="0" vspace="0"> <tbody> <tr> <td style="text-align: justify;">In this paper, design and fabrication of a diode pumped Er-Yb:Glass laser Q-switched with Co²⁺:MgAl₂O₄ crystals was reported. The LASCAD software was used for designing the laser and based on this design; a laboratory layout was set up. Finally, the laser pulses of duration 30 ns and energy 15 mJ at about 2 W of incident pump power was obtained experimentally.</td> </tr> </tbody> </table> <div style="clear:both;"></div> لیزر Er-Yb:Glass, بلورCo2+:MgAl2O4 , جاذب اشباع‌پذیر, دمش از پهلو. Er-Yb:Glass laser, Co2+:MgAl2O4 crystals, Saturable absorber, Side pumped. 493 496 http://opsi.ir/browse.php?a_code=A-10-1-1458&slc_lang=fa&sid=1 Marziyeh Karmand مرضیه کارمند 10031947532846006603 10031947532846006603 Yes Department of Physics, Shiraz University of Technology دانشگاه صنعتی شیراز Gholamreza Honarasa غلامرضا هنرآسا 10031947532846006604 10031947532846006604 No Department of Physics, Shiraz University of Technology دانشگاه صنعتی شیراز Amir Noferesti امیر نوفرستی 10031947532846006605 10031947532846006605 No Department of Physics, Shiraz University of Technology دانشگاه صنعتی شیراز Mahdi Bahadoran مهدی بهادران 10031947532846006606 10031947532846006606 No Department of Physics, Shiraz University of Technology دانشگاه صنعتی شیراز